Uniform and dry SiO2 beads

Encapsulator B-390 / B-395 Pro: Manufacturing of dry spherical monodisperse SiO2 beads with a size of 430 μm
Uniform and dry SiO2 beads
Advanced ceramic materials are of high interest due to their specific and favorable properties such as hardness, durability, optical behavior compared to traditional materials. SiO2 among other oxides such as Al2O3, TiO2 and ZrO2, are common raw materials. In the manufacturing process of advanced materials, granulation is one of the important steps. Usually, large and uniform particles are desired.This application note describes the production of spherical and uniform SiO2 beads having an average size of approximately 430 μm in diameter. The Encapsulator B-395 Pro was applied to obtain and the Rotavapor® R-300 to dry the beads. Using the presented technique, the particle size of the final beads can be varied in the range between 300 and 1000 μm.

ลงทะเบียนเพื่อดาวน์โหลด

ประเทศ
บูชิต้องการส่งข้อมูลอื่น ๆ ที่เกี่ยวข้องถึงคุณในอนาคต เช่น แอพพริเคชันโน๊ต, ไกด์บุ๊ค, การสัมมนาผ่านออนไลน์และคำเชิญเข้าร่วมสัมมนาซึ่งคุณอาจสนใจ ดังนั้นทางบูชิจึงต้องการขอความยินยอมจากคุณเพื่อการติดต่อ คุณสามารถค้นหาเกี่ยวกับสิทธิ์ของคุณและวิธีที่เราใช้และประมวลผลข้อมูลส่วนบุคคลของคุณได้ใน นโยบายความเป็นส่วนตัว

เครื่องมือที่เกี่ยวข้อง

Similar Applications